P 金屬粉末 RDOUCT
Refers to as the base, iron, nickel and cobalt in the high temperature of 600 ℃ above and must be long-term work stress environment of metal materials, has high temperature strength, good resistance to corrosion resistance and oxidation resistance and good plasticity and toughness; Mainly used in high performance engines, in the modern advanced aircraft engine, high temperature alloy material usage accounts for 40% ~ 60% of engine total quality, but also widely used in nuclear power, chemical, and other fields.
High temperature alloy powder morphology under electron microscope
牌號 | 化學成分 | 產品標準 | 粒度分布 | ||
主元素 | 雜質元素 | 國標 | 美標 | ||
IN625 (GH3625) |
Cr：20.0-23.0 Mo：8.0-10.0 Nb：3.15-4.15 Fe：≤5.0 Si：≤0.50 Ni：Bal |
Ti：≤0.40 Al：≤0.40 C：≤0.10 Co：≤1.00 S：≤0.015 P：≤0.015 O：≤0.01 | GB/T 14992-2005 | 15-45μm 15-53μm 53-120μm 53-150μm | |
IN718 (GH4169) |
Ni：50.0-55.0 Cr：17.0-21.0 Nb：4.75-5.25 Mo：2.80-3.30 Ti：0.65-1.15 Al：0.20-0.80 Cu：≤0.30 Fe：Bal
|
O：≤0.01 | GB/T 14992-2005 | 15-45μm 15-53μm 53-120μm 53-150μm | |
In713C （K418） |
Cr：11.5-13.5 Mo：3.8-4.8 Al：5.5-6.4 Ti：0.5-1.0 Nb：1.8-2.5 Ni：Bal
|
C：0.08-0.16 Fe：≤1.0 O：≤0.01
| GB/T 14992-2005 | 15-45μm 15-53μm 53-120μm 53-150μm | |
IN939 |
Cr：21.5-23.5 Co：18-20 W：1.8-2.2 Nb：0.8-1.2 Ta：1.2-1.6 Ti：3.5-3.9 Al：1.7-2.1 Zr：0.05-0.14 Ni：Bal
|
C：0.13-0.18 B：0.004-0.015 O：≤0.003
| GB/T 14992-2005 | 15-45μm 15-53μm 53-120μm 53-150μm | |
K4648 |
Cr：32.0-35.0 W：4.3-5.5 Mo：2.3-3.5 Al：0.7-1.3 Nb：0.7-1.3 Fe：≤0.5 C：0.03-0.1 |
B：≤0.008 Ce：≤0.030 Si：≤0.30 S：≤0.01 Y：≤0.04 Ca：≤0.02 O：≤0.02 | GB/T 14992-2005 | 15-45μm 15-53μm 53-120μm 53-150μm O：≤0.01 | |